Pengaruh Variasi Komposisi Agregat Kasar Terhadap Kuat Tekan dan Penyerapan Air Paving Block
DOI:
https://doi.org/10.55123/insologi.v2i5.2667Keywords:
Paving Block, Compressive Strength, Water Absorption, Coarse AggregateAbstract
According to SNI 03-0691-1996, paving block is a composition of building materials made from a mixture of portland cement or similar hydraulic adhesive materials, water and aggregate with or without other additives. Pavement construction in Indonesia mostly uses natural aggregates or crushed stone that has a rough and angular surface so that it has excellent adhesion to the concrete. The purpose of this study is to evaluate the effect of the addition of crushed stone on the compressive strength and water absorption of concrete paving blocks, compared with paving blocks of mortar. Paving block test samples were made with 5 variations of composition of cement:sand:crushed stone, namely 1:4:0, 1:4:1, 1:4:2, 1:4:3 and 1:4:4. Each composition was made as test samples of blocks with a size of 20 cm × 10 cm × 6 cm. The test results showed that the average compressive strength of paving blocks with the composition of 1:4:0, 1:4:1 and 1:4:4 was less than 8,5 MPa and water absorption is greater than 10%; thus, they were not classified as paving blocks with grade D. While, the paving blocks with the composition of 1:4:2 and 1:4:3 were classified as paving blocks with grade D.
Downloads
References
Badan Standarisasi Nasional, 2012, Metode Uji Bahan yang Lebih Halus dengan Saringan 75 (No. 200) dalam Agregat Mineral dengan Pencucian (SNI ASTM C117:2012), Jakarta, Indonesia.
Badan Standarisasi Nasional, 2012, Metode Uji Untuk Analisis Saringan Agregat Halus dan Agregat Kasar (ASTM C136-06, IDT), Jakarta: Badan Standardisasi Nasional Indonesia.
Badan Standarisasi Nasional, 1996, Persyaratan mutu bata beton (paving block) (SNI 03-0691-1996), Jakarta, Indonesia.
Akhmad, F. I. (2022). Pengaruh Penggunaan Kerikil Jagung Sebagai Bahan Pengganti Sebagian Pasir Pada Paving Block. 1–107.
Etri Suhelmidawati. (2022). the Utilization of Limestone Waste Sand/Gravel in Concrete Block Paving Mixture. 17–24.
Mallisa, H. (2006). PENGARUH BATU PECAH TERHADAP KUAT TEKAN PAVING BLOCK. SMARtek, 4(3), 156–165.
Pratiwi, I., & Yanti, E. D. (2018). Pengaruh zeolit sebagai agregat kasar dan abu batubara sebagai bahan campuran semen terhadap kuat tekan paving block. Jurnal Teknologi Mineral Dan Batubara, 14(3), 187–194. https://doi.org/10.30556/jtmb.vol14.no3.2018.158
Rakhmawati, A., & Amin, M. (2010). kulit kerang sebagai bahan substitusi agregat kasar untuk paving block sesuai SII 0819-83. Fakultas Teknik Universitas Tidar Magelang, 34(2), 175–189.
Sasmita, G. (2012). PENGUJIAN KUAT TEKAN PAVING BLOCK MENGGUNAKAN LIMBAH BATU KAPUR SEBAGAI PENGGANTI AGREGAT. Diploma, Program Teknik, I I I Sipil, Jurusan Teknik Teknik, Fakultas Jember, Universitas.
SNI 7656-2012. Rancangan Campuran Beton. Badan Standarisasi Nasional. Jakarta.
SNI 03-2834-2000. Klasifikasi Daerah Gradasi Pasir. Badan Standarisasi Nasional. Jakarta.
SNI (2004). SNI 15-7064-2004. Semen Portland Komposit. Badan Standarisasi Nasional. Jakarta.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2023 Dera Anggun Saputri, Syafri Wardi, Angelalia Roza
This work is licensed under a Creative Commons Attribution 4.0 International License.
Hak cipta pada setiap artikel adalah milik penulis.
Penulis mengakui bahwa INSOLOGI (Jurnal Sains dan Teknologi) sebagai publisher yang mempublikasikan pertama kali dengan lisensi Creative Commons Attribution 4.0 International License.
Penulis dapat memasukan tulisan secara terpisah, mengatur distribusi non-ekskulif dari naskah yang telah terbit di jurnal ini kedalam versi yang lain, seperti: dikirim ke respository institusi penulis, publikasi kedalam buku, dan lain-lain. Dengan mengakui bahwa naskah telah terbit pertama kali pada INSOLOGI (Jurnal Sains dan Teknologi).