Pelindian Fe₂O₃ dari Limbah Karat Besi Menggunakan HCl dan H₂C₂O₄
DOI:
https://doi.org/10.55123/insologi.v4i1.4861Keywords:
Fe₂O₃, Leaching, Precipitation, HCl, H₂C₂O₄, Iron Rust WasteAbstract
This study aims to extract iron(III) oxide (Fe₂O₃) from iron rust waste using a leaching method with hydrochloric acid (HCl) and oxalic acid (H₂C₂O₄). After the leaching process with acids, precipitation was carried out using sodium hydroxide (NaOH) solution. The variation in acid type was conducted to evaluate the leaching effectiveness based on the Fe₂O₃ yield obtained. The results showed that HCl was more effective in dissolving Fe₂O₃ compared to H₂C₂O₄. The yields obtained from each acid type were 64.44% for HCl and 24.39% for H₂C₂O₄. The precipitation process was performed at a pH of 5–7 to ensure the formation of a stable Fe(OH)₃ precipitate before being dried into Fe₂O₃. Qualitative analysis using potassium hexacyanoferrate(III) (K₄[Fe(CN)₆]) confirmed the presence of Fe³⁺ ions in the final product from both acid treatments. This method has proven to be effective in obtaining high-quality Fe₂O₃ that can be used in various industrial and research applications. Additionally, this study contributes to the utilization of iron rust waste as a valuable precursor material for direct use or further processing while also reducing environmental pollution.
Downloads
References
Antara, N. L. (2013). Pencegahan Akibat Terjadinya Karat Pada Pipa Boiler. Jurnal Logic, Vol. 3, No. 3.
Darmawan, P., Herawati, D. A., & Wibawa, D. A. (Januari 2025). Penentuan Kadar Garam Halogenida pada Larutan Dua Garamnya dengan Metode Gravimetri. Jurnal Kimia dan Rekayasa, Volume 5 Nomor 2.
Febrina, L., & Ayuna, A. (2015). Studi Penurunan Kadar Besi (Fe) dan Mangan (Mn) dalam Air Tanah Menggunakan Saringan Keramik. Jurnal Teknologi, Volume 7 No.1.
Khalamudilah, F. A., Suhendar, D., & Supriadin, A. (2017). Sintesis dan Karakterisasi Pigmen Merah Besi(III) Oksida dari Serbuk Besi Limbah Bubut Logam. Jurnal al-Kimiya, 45-50.
Kheloufi, A., Berbar, Y., Kefaifi, A., Medjahed, S. A., & Kerkar, F. (2011). Improvement of Impurities Removal from Silica Sand by Using a Leaching Process. Chemical Engineering Transactions, 1513-1537.
Khoiroh, L. M., Mardiana, D., Sabarudin, A., & Ismuyanto, B. (2013). Synthesis of Hematit Pigments (a-Fe2O3) by Thermal Transformation of FeOOH. Journal of Pure Applied Chemistry, 27-34.
Lopez, Y. F. (2023). Elektrokimia: Korosi dan Pencegahannya. Kupang: Politeknik Pertanian Negeri Kupang.
Novia, F. A., Rukmananda, B. W., Juwairi, & Anugrah, R. P. (2021). Pra Rancangan Pabrik Pigmen Merah dengan Metode Presipitasi. Journal of Fundamentals and Application of Chemical Engineering, Vol. 02, No. 01.
Prasetyo, A. B., Prasetiyo, P., & Matahari, I. (2014). Pembuatan a-Fe2O3 dari Hasil Pengolahan Bijih Besi Primer Jenis Hematit untuk Bahan Baku Baterai Lithium. Majalah Metalurgi, 179-190.
Priyambudi, I. Y., Amrullah, M. R., Poerwadi, B., & Oktavian, R. (2017). Aplikasi Katalis Heterogen Fe2O3-CaO pada Pembuatan Biodiesel dari Minyak Kelapa Sawit. Jurnal Mahasiswa Teknik Kimia, Vol. 2 No. 4.
Publik, B. K. (2023, Juli 12). Retrieved from Fakultas Teknik Universitas Indonesia: https://eng.ui.ac.id/korosi-sebabkan-kerugian-ekonomi-dan-kesehatan-guru-besar-ftui-prof-rini-riastuti-telaah-upaya-pencegahannya/?utm_source=chatgpt.com
Rame, Purwanto, A., & Budiarto, A. (2017). Pengolahan air limbah tekstil berbasis ozonisasi katalitik dengan katalis besi(III) oksida (Fe2O3) dan aluminium oksida (Al2O3) menggunakan difuser mikro. Jurnal Riset Teknologi Pencegahan Pencemaran Industri, 67-75.
Riskawati, Amir, R., & Muin, H. (2019). Efektivitas Arang Sekam Padi Dalam Menurunkan Kadar Besi (Fe) Pada Air Sumus Bor di Desa Padangloang Kabupaten Pinrang. Jurnal Ilmiah Manusia dan Kesehatan, Vol. 2, No. 1.
Rosbiono, M. (2020). Terminologi-Karakteristik-Metode Pendeteksian-Aplikasi, Klasifikasi, Tatanama dan Isomerisasi Senyawa Koordinasi. In Kimia Koordinasi 3. Universitas Terbuka.
Saugi, W. (2021). Pengaruh Faktor Fisik, Kimia, dan Biologi Medium Terhadap Laju Korosi Besi. Borneo Journal of Science and Mthematics Education, Vol. 1 No.1.
Setyo, S. B., Sulistyaningsih, T., Prasetya, A. T., & Kusumastuti, E. (2021). Iron Extraction from Coal Fly Ash Using HCl Solution. Indonesian Journal of Chemical Science.
Shen, L., Qiao, Y., Guo, Y., & Tan, J. (2013). Preparation and Formation mechanism of nano-iron oxide black pigment from blast furnace flue dust. Ceramics International, 39, 737-744.
Vogel, A. (1979). Textbook Macro and Semimicro Qualitative Inorganic Analysis. New York: Longman Inc.
Yoon, S., & Bae, S. (2018). Novel synthesis of nanoscale zerovalent iron from coal fly ash and its application in oxidative degradation of methyl orange by Fenton reaction. Journal of Hazardous Materials.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2025 Asiyah Nurrahmajanti
This work is licensed under a Creative Commons Attribution 4.0 International License.
Hak cipta pada setiap artikel adalah milik penulis.
Penulis mengakui bahwa INSOLOGI (Jurnal Sains dan Teknologi) sebagai publisher yang mempublikasikan pertama kali dengan lisensi Creative Commons Attribution 4.0 International License.
Penulis dapat memasukan tulisan secara terpisah, mengatur distribusi non-ekskulif dari naskah yang telah terbit di jurnal ini kedalam versi yang lain, seperti: dikirim ke respository institusi penulis, publikasi kedalam buku, dan lain-lain. Dengan mengakui bahwa naskah telah terbit pertama kali pada INSOLOGI (Jurnal Sains dan Teknologi).